Drop File

• Resin Type:  PLA
• Density: 1.24 g/cm³
• Vicat Softening Temperature: 57 °C
• Heat Deflection Temperature: 57 °C
• Melting Temperature: 160 °C
• Melt Index: 42.4 ± 3.5 g/10 min
• Tensile Strength: 39 ± 2 MPa
• Breaking Elongation Rate: 12.2 ± 0.4 %
• Bending Modulus: 2750 ± 60 MPa
• Bending Strength: 76 ± 3 MPa
• Impact Strength: 26.6 ± 2.8 kJ/m²

• PETG 3D-utskriftsmaterialet är mycket lätt att bearbeta
• Komponenterna är extremt starka, hållbara och långvariga.
• Vattenavvisande material (hydrofobt: absorberar inte vatten)
• I den klara versionen godkänd för kontakt med livsmedel (livsmedelssäker)
• Ingen obehaglig lukt under bearbetningen

• Resin Type:  PET-G
• Density: 1.27 g/cm³
• Vicat Softening Temperature: ? °C
• Heat Deflection Temperature: ? °C
• Melting Temperature: ? °C
• Melt Index: ? g/10 min
• Tensile Strength: 50 MPa
• Breaking Elongation Rate: 23 %
• Bending Modulus: 2150 MPa
• Bending Strength: ? MPa
• Impact Strength: 81 kJ/m²

• PETG 3D-utskriftsmaterialet är mycket lätt att bearbeta
• Komponenterna är extremt starka, hållbara och långvariga.
• Vattenavvisande material (hydrofobt: absorberar inte vatten)
• I den klara versionen godkänd för kontakt med livsmedel (livsmedelssäker)
• Ingen obehaglig lukt under bearbetningen

• Resin Type:  PET-G
• Density: 1.27 g/cm³
• Vicat Softening Temperature: ? °C
• Heat Deflection Temperature: ? °C
• Melting Temperature: ? °C
• Melt Index: ? g/10 min
• Tensile Strength: 50 MPa
• Breaking Elongation Rate: 23 %
• Bending Modulus: 2150 MPa
• Bending Strength: ? MPa
• Impact Strength: 81 kJ/m²

PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.

• Resin Type:  PAHT-CF
• Density: 1.06 g/cm³
• Vicat Softening Temperature: 220 °C
• Heat Deflection Temperature: 194 °C
• Melting Temperature: 225 °C
• Melt Index: 14.4 ± 2.0 g/10 min
• Tensile Strength: 88 ± 7 MPa
• Breaking Elongation Rate: 10.4 ± 0.7 %
• Bending Modulus: 4120 ± 290 MPa
• Bending Strength: 140 ± 8 MPa
• Impact Strength: 57.5 ± 3.4 kJ/m²

• Similar to ABS thermoplastic materials, the resin has good toughness, excellent impact strength and high mechanical properties, strong scratch resistance, is not brittle, can drill holes, suitable for printing tough industrial parts.
• ABS-like resins contain high-quality pigments and photoinitiators, so the models printed with resin have a very pure and stunning color effect, just like works of art.

• With a wide range of applications from tabletop models to industrial parts that require a certain strength or toughness.

• Resin Type:  ABS-like resin V2.0
• Hardness: 84 D; Shrinkage: 7.1 %
• Viscosity (25°C): 150-200 mPa.s
• Liquid Density: 1.100 g/cm³
• Solid Density: 1.195 g/cm³
• Flexure Strength: 59-70 Mpa
• Extension Strength: 36-53 Mpa
• Elongation at Break: 14.2 %